Swan LSZH XLPE PVC Compound Cable Grade Compound

• Application: Electrical Winding Insulation, Electrical Base, Shell
• Type: XLPE Compound
• Chemistry: Cross-Link
• Material: Polyolefin
• Classification: XLPE Compound
• Certification: ISO9001
• Model NO.: Compound
• Color: Customized According to Customer Requirements
• Brand: Swan
• Appearance: 4X 3 mm
• Gel Content: ≥60
• Tensile Strength: ≥13.5
• Elongation at Break: ≥350
• Brittleness Temperature: ≤15
• Hot Set Elongation Elongation Under Load: ≤80
• Permanent Deformation After Cooling: ≤5
• Change of Tensile Strength: ≤±20
• Change of Elongation: ≤±20
• DC Volume Resistivity (20ºC): ≥1.0X1014
• Dielectric Strength(20ºC): ≥25
• Transport Package: 25kg/Bag
• Trademark: SWAN
• Origin: China
• Production Capacity: 20000ton/Year

Product Description

CAR-1255P 125ºC e-beam cross-linkable halogen-free flame-retardant polyolefin for automobile wire

Product Description

 

  CAR-1255P is based on special polyolefin, containing special environmental flame retardant, antioxidant, cross-linking agent and other additives. It is a kind of granular plastic produced by precise mixing and granulation with special formula.

Product Parameters

Properties	Units	CAR-1255P
		Standards	Typical values
Tensile strength before irradiation	MPa	≥10.0	15.0
Elongation at break before irradiation	%	≥150	300
Tensile strength after irradiation	MPa	≥12.0	16.5
Elongation at break after irradiation	%	≥150	210
Aging test in air oven (155±2ºC×168h)
- Retention rate of elongation at break	%	≥80	105
- Retention rate of tensile strength	%	≥50	92
Hot set value (200ºC, 0.2 MPa, 15min)
- Elongation under load, Max.	%	≤175	40
- Permanent elongation after cooling, Max.	%	≤15	0
Low-temperature impact embrittlement	ºC	-40ºCpass	pass
Volume resistivity at 20ºC	Ω·m	1.0×1011	2.7×1013
Dielectric strength	MV/m	≥20	29
Density	g/cm3	-	1.39
LOI (A method)		≥24	28
Hardness (shore D)	D	-	62±2